Page 12 - KeyFireCatalog2010

• Rubber Covered Hose
• 13/4 ” and 2 1 /2 ” Hi-Rise Hose
a Scope
Quality: The fire hose assembly supplied under this spec-
ification shall be constructed with superior quality materials.
NFPA 1961 standards shall be observed in production of the
assembly, in order to ensure its quality and durability.
Warranty: Pro-Lite hose shall carry a 5 year warranty
against defects in material and workmanship. Barring any
mistreatment or accidental damage the warranted hose
will be replaced at no charge.
Note: This hose is specifically designed for high-rise use.
a Hose Construction
Hose shall be made from 100 percent high tenacity syn-
thetic yarn, circularly woven and completely protected
and locked-in by tough highly resistant synthetic nitrile
rubber, forming a single homogeneous construction with-
out the use of glues or adhesives of any type.
a Lining Properties
Ultimate Tensile Strength: Tensile strength of the
lining and cover shall not be less than 2000 PSI.
Ultimate Elongation: 400 percent minimum.
Accelerated Aging Test: The tensile strength and
ultimate elongation of the vulcanized rubber compound
which has been subjected to the action of oxygen at a
pressure of 300 PSI (±10PSI) and a temperature of
158°(±18°)F for a period of 96 hours shall retain 60 per-
cent of its originally stated properties.
a Hydrostatic Pressure Test
Service Test Acceptance Burst
Part # Diameter Pressure Test Pressure Pressure
RC17-600SO 13/4” 300psi 600psi 900psi
RC25-600SO 21/2” 300psi 600psi 900psi
a Abrasion Resistance
Hose shall withstand 5,000 cycles on the Taber Abrasion
Machine (H-22 Wheel: 1 kg). Key Fire Hose Corporation on
request will supply written warranties that PRO-LITE hose
meets a minimum 5,000 cycles. Other abrasion test results
(UL, DIN, etc.) can be supplied on request of purchaser.
a Cold Resistance
Hose shall have a capability of use down to -35°F. Hose shall
have no apparent damage to cover, reinforcement or lining
when subjected to the following cold bending test: a 50 ft.
length of dry hose is to be firmly coiled and placed in a cold box
at -35°F for a duration of 24 hours. Immediately after removal
of the hose from the box, hose should be uncoiled and laid out
by one operator. Following this procedure, the hose shall not
PHONE 1-800-447-5666 • FAX 1-800-447-5664 • E-MAIL sales@keyfire.com
leak nor show any damage to the reinforcement when sub-
jected to the hydrostatic acceptance test stated above.
a Ozone Resistance
Hose shall show no visible signs of cracking to the lining
or cover when tested in accordance to ASTM D518
Procedure B (100pphm/118°F/70 hours).
a Chemical Resistance
Exposure to sea water and contamination by most
chemical substances, hydrocarbons, oils, alkalis, acids
and greases must have no effect on the short or long
term performance of the hose. A chemical resistance
chart is available and Key Fire Hose will supply specific
chemical resistance data on request of purchaser for
unique applications.
a Heat Resistance
The hose, when subjected to a static pressure of 100 PSI,
shall be capable of withstanding a surface temperature of
1200°F for a minimum of two minutes without rupture
or damage to the synthetic reinforcement.
a Hose Weight and Coil Diameters
The hose shall conform to the following average weights
and diameters
Coil Size-Coupled
Part # Diameter Weight per Foot per 50’ Lengths
RC17-600SO 13/4” .2 lbs 10 in.
RC25-600SO 21/2” .4 lbs 14 in.
a Color
The color shall be HI-VISIBILITY orange.
a Couplings
As required by purchaser.
Key reserves the right to modify any specification with-
out prior notice to meet or exceed changing standards.
Customers are advised that special diameters or con-
struction characteristics can be produced on special
request and you are requested to contact Key Fire Hose
Corporation, Miami, Florida.
Visit us on the Web: www.keyfire.com
01/04 KF-014